Self-Healing Polymer Network with High Strength, Tunable Properties, and Biocompatibility




Diggle, Broden
Jiang, Zhen
Li, Rachel
Connal, Luke

Journal Title

Journal ISSN

Volume Title


American Chemical Society


Nature has designed and optimized materials to possess a range of properties and functions. Here, we introduced a molecular design strategy to impart customizable functionality and varying mechanical properties into gels; mimicking nature's range of tunable materials. We demonstrate a gel that is not only tough but also exhibits self-healing, is easily controllable, and the final materials have a broad range of mechanical properties. To develop these materials, we first prepared a methacrylic acid (MAAc) and poly(ethylene glycol) methyl ether methacrylate (OEGMA) random copolymer: poly(MAAc-co-OEGMA). The network's deliberate inter- and intramolecular hydrogen bondings were modified through some of the acid sites being postfunctionalized with benzaldehyde (BA) and cross-linked with diamine-terminated poly(dimethylsiloxane) (PDMS) to form dynamic imine bonds. Due to the low glass transition temperature of the PDMS cross-linker, the chain mobility can be enhanced, enabling rapid self-healing (>98% within seconds), in addition to improving the stretchability (tensile strain) from a few % to almost 500%. The prepared polymers and gels were well characterized through various techniques including Fourier transform infrared spectroscopy (FTIR), 1H NMR, and size-exclusion chromatography (SEC) analysis. Mechanical testing and dynamic mechanical analysis (DMA) revealed interesting insights into the broad-range (Young's modulus: 100 kPa to >300 MPa) and tunable mechanical properties, including the tensile strength (from 12 to 0.1 MPa) and strain (up to 500%) as well as the storage (0.1 to 60 MPa) and loss (1 to 40 MPa) moduli of the dynamic self-healing gel. Interestingly, the tensile strength decreasing with increasing cross-link density. Lastly, the biocompatibility of the gels was investigated, with an initial study of both human bone and skin cells indicating increased biocompatibility with gels that had been cross-linked with PDMS.





Chemistry of Materials


Journal article

Book Title

Entity type

Access Statement

Open Access

License Rights



Restricted until