Fabrication and characterization of bare Ge-Sb-Se chalcogenide glass fiber taper

Abstract

In this work, Ge15Sb20Se65 bare glass fiber with a diameter of 500 μm was fabricated, and then tapered with different tapering parameters. The analysis of Raman and energy dispersive X-ray spectra (EDS) indicated that, a slight change in the chemical composition of the glass, fiber and tapering fiber has negligible effect on the glass structure. It was found that, the waist diameter decreases exponentially with increasing tapering length and speed, and high quality taper fiber with the cone diameter of 2.65 μm can be achieved under the optimal tapering conditions. Finally, the simulated and experimental results of the output transmission under different waist length and taper ratio show that the transmission decreases with increasing waist length and taper ratio Show more