Microstructure and mechanical properties of 80Ni20Cr alloy manufactured by laser 3D printing technology
Date
2017
Authors
Tan, Shu-jie
Li, Duosheng
Qin, Qinghua
Liu, Hong-bing
liao, Xiaojun
Jiang, Lei
Journal Title
Journal ISSN
Volume Title
Publisher
Nonferrous Metals Society of China/Zhongguo Youse Jinshu Xuehui
Abstract
80Ni20Cr alloy was manufactured by laser 3D printing technology using two different laser 3D printing routes, namely, layer-layer orthogonal and layer-layer with the same direction, and the microstructure and mechanical properties of 80Ni20Cr alloy were also studied. The results show that the microstructures of alloy components present small lamellar grains and columnar grains, and the columnar grains grow along the path of laser 3D printing route. The composition of the alloy components is Ni-Cr solid solution based Ni solvent. Moreover, the density of 80Ni20Cr alloy manufactured by laser 3D printing is close to the theoretical density of alloy. The porosity of 80Ni20Cr alloy fabricated by laser 3D printing technology using layer-layer orthogonal route is lower than that of layer-layer with the same direction, meanwhile, the average micro-hardness and tensile properties of 80Ni20Cr alloy components using layer-layer orthogonal route are also higher than that of using layer-layer with the same direction, and the tensile strength of alloy reaches up to 410 MPa, the hardness of alloy reaches up to 406 HV0.2.
Description
Keywords
3D printing, 80Ni20Cr alloy, microstructure, mechanical properties, porosity
Citation
Collections
Source
Zhongguo Youse Jinshu Xuebao = Chinese Journal of Nonferrous Metals
Type
Journal article
Book Title
Entity type
Access Statement
License Rights
Restricted until
2099-12-31
Downloads
File
Description