Haberl, BiancaLiu, A. C. Y.Bradby, JodieRuffell, SimonWilliams, JamesMunroe, Paul2015-12-102015-12-101098-0121http://hdl.handle.net/1885/39881We investigate the structure and mechanical properties of pressure-induced (PI) amorphous silicon (a-Si) and compare this to the more extensively characterized case of a-Si created by ion implantation. To study the effect of thermal history we also examine the structure of both PI and ion-implanted a-Si after a low-temperature "relaxation" anneal (450°C). Indentation testing suggests that structural changes are induced by thermal annealing. As-prepared forms of a-Si deform via plastic flow, while relaxed forms of a-Si transform to high-pressure crystalline phases. These structural changes are confirmed by more explicit measurements. Raman microspectroscopy shows that the short-range order as expressed by the average bond-angle distortion of the as-prepared amorphous phases is the same and reduced by the same amount following the low-temperature anneal. Fluctuation electron microscopy demonstrates that the as-prepared PI a-Si displays a much lower variance of the diffracted intensity, a feature directly correlated with the medium-range order, than the as-prepared ion-implanted a-Si. However, relaxation brings this variance of the two networks to the same intermediate level. The mechanical tests and structural probes indicate that annealing the amorphous silicon network can bring it to a common state with the same structure and properties regardless of the initial state. This final state might be the closest attainable to the continuous random network model.200910.1103/PhysRevB.79.1552092015-12-09