Glushenkov, AZhang, Hong-ZhouChen, Ying2015-12-082015-12-080167-577Xhttp://hdl.handle.net/1885/35050ZnO powder showed anomalous evaporation behavior after its mechanical milling treatment under high-energy conditions. The amount of generated vapor is about 10 times higher in the first 15 min of annealing at 1300 °C than that of unmilled ZnO powders.Keywords: Ball milling; Crystal structure; Evaporation; Grain boundaries; Powders; Vapors; Anomalous evaporation; Heavily milled material; Mechanical milling treatment; Weakly bonded atoms; Zinc oxide Ball milling; Crystal structure; Defects; Evaporation; Zinc oxide200810.1016/j.matlet.2007.06.0392015-12-08