Khosravifar, MahnooshMirkazemi, Seyyed MohammadTaheri, MahdiarGolestanifard, Farhad2023-09-011544-1024http://hdl.handle.net/1885/297204In this study, to produce electrically conductive ceramics, rapid hot press (RHP) sintering of 3 mol.% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) and 3Y-TZP/TiN composites with TiN amounts of 25, 35, and 45 vol.% was performed at 1300, 1350, and 1400 A degrees C. Interestingly, the toughness and hardness were improved in the presence of TiN up to 35 vol.% and maximum fracture toughness and hardness of 5.40 +/- 0.05 MPa m(1/2) and 14.50 +/- 0.06 GPa, respectively, were obtained. However, the bending strength was decreased which could be attributed to the rather weak interfaces of nitride and oxide phases. Regarding the zirconia matrix, the effect of grain size on fracture toughness of the samples has been studied using x-ray diffraction and field emission scanning electron microscope (FESEM) analysis. It was also found that electrical resistivity decreased to the value of 6.88 x 10(-6) Omega m at 45 vol.% of TiN. It seems the TiN grains form a network to impose conductivity on the ZrO2 body; however, below 35 vol.% TiN, due to lack of percolation effect, this conductivity could not be maintained according to FESEM studies. Finally, electrically conductive samples were successfully machined by electrical discharge machining (EDM).application/pdfen-AU© ASM International3 mol.% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP)3Y-TZP/TiN compositeselectrical conductivityelectrical discharge machining (EDM)mechanical propertiestitanium nitride201810.1007/s11665-018-3173-52022-07-24