Mahmud, Md ArafatDuong, TheYin, YantingPham, Huyen T.Walter, DanielPeng, JunWu, YiliangLi, LiShen, HepingWu, NandiMozaffari, NaeimehAndersson, GuntherCatchpole, KylieWeber, KlausWhite, Thomas2021-11-122021-11-121616-301Xhttp://hdl.handle.net/1885/251762Defect-mediated carrier recombination at the interfaces between perovskite and neighboring charge transport layers limits the efficiency of most state-of-the-art perovskite solar cells. Passivation of interfacial defects is thus essential for attaining cell efficiencies close to the theoretical limit. In this work, a novel double-sided passivation of 3D perovskite films is demonstrated with thin surface layers of bulky organic cation–based halide compound forming 2D layered perovskite. Highly efficient (22.77%) mixed-dimensional perovskite devices with a remarkable open-circuit voltage of 1.2 V are reported for a perovskite film having an optical bandgap of ≈1.6 eV. Using a combination of experimental and numerical analyses, it is shown that the double-sided surface layers provide effective defect passivation at both the electron and hole transport layer interfaces, suppressing surface recombination on both sides of the active layer. Despite the semi-insulating nature of the passivation layers, an increase in the fill factor of optimized cells is observed. The efficient carrier extraction is explained by incomplete surface coverage of the 2D perovskite layer, allowing charge transport through localized unpassivated regions, similar to tunnel-oxide passivation layers used in silicon photovoltaics. Optimization of the defect passivation properties of these films has the potential to further increase cell efficiencies.The work was supported by the Australian Government through the Australian Renewable Energy Agency (ARENA) and the Australian Research Council (ARC). T.P.W. is the recipient of an Australian Research Council Future Fellowship (Project No. FT180100302) funded by the Australian Government.application/pdfen-AU© 2019 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheimmixed-dimensional perovskitepassivationsolar cellssurface bandgap wideningDouble‐Sided Surface Passivation of 3D Perovskite Film for High‐Efficiency Mixed‐Dimensional Perovskite Solar Cells2020-02-1210.1002/adfm.201907962