High performance Bi₀.₅Na₀.₅TiO₃-BiAlO₃-K₀.₅Na₀.₅NbO₃ lead-free pyroelectric ceramics for thermal detectors

Abstract

Both high pyroelectric properties and good temperature stability of ferroelectric materials are desirable when used for applications in infrared thermal detectors. In this work, we report lead-free ternary 0.97(0.99Bi0.5Na0.5TiO3-0.01BiAlO3)-0.03K0.5Na0.5NbO3 (BNT-BA-KNN) ceramics, which not only exhibits a large pyroelectric coefficient (p ∼ 3.7 × 10-8 C cm-2K-1) and figures of merit (Fi, Fv, and Fd) but also shows excellent thermal stable properties. At room temperature, Fi, Fv, and Fd are determined as high as 1.32 × 10-10 m/V, 2.89 × 10-2 m2/C, and 1.15 × 10-5Pa-1/2 at 1 kHz and 1.32 × 10-10 m/V, 2.70 × 10-2 m2/C, and 1.09 × 10-5Pa-1/2 at 20 Hz, respectively. During the temperature range of RT to 85 °C, the achieved p, Fi, Fv, and Fd do not vary too much. The high depolarization temperature and the undispersed ferroelectric-ergodic relaxor phase transition with a sharp pyroelectric coefficient peak value of ∼400 × 10-8 C cm-2K-1 are suggested to be responsible for this thermal stability, which ensures reliable actual operation. The results reveal the BNT-BA-KNN ceramics as promising lead-free candidates for infrared thermal detector applications. Show more