Investigation of the thermal stability of MoOx as hole-selective contacts for Si solar cells
Date
2018
Authors
Zhang, Tian
Lee, Chang-Yeh
Wan, Yimao
Lim, Sean
Hoex, Bram
Journal Title
Journal ISSN
Volume Title
Publisher
American Institute of Physics (AIP)
Abstract
The stoichiometry and work function of molybdenum oxide (MoOx) are of crucial importance for its performance as hole selective contact for crystalline silicon solar cells. Hydrogenated amorphous silicon (a-Si:H) is typically used as an interface passivation layer in combination with MoOx to reduce surface recombination. As the fabrication process of a solar cell typically contains subsequent high-temperature processes, the consideration of thermal stability of MoOx with and without a-Si:H becomes critical. In this work, in situ x-ray spectroscopy (XPS)/ultraviolet photoelectron spectroscopy and Fourier transform infrared spectroscopy in the temperature range from 300 K to 900 K are used to investigate the thermal stability of MoOx with and without a-Si:H. In addition, both the passivation and contact performance are studied by evaluating the surface saturation current density J0s, carrier lifetime τeff, and contact resistivity ρc. The XPS results reveal that the as-evaporated MoOx on top of both c-Si and a-Si:H is sub-stoichiometric, and the work function of both films is higher than 6 eV. While after in situ annealing, the evolution of MoOx phase on top of a-Si:H shows a different behavior compared to it on c-Si which is attributed to H diffusion from a-Si:H after 600 K, whereas the work function shows a similar trend as a function of the annealing temperature. The J0s of a p-type Si symmetrically passivated by MoOx is found to be 187 fA/cm2 and the ρc is ∼82.5 mΩ·cm2 in the as-evaporated state. With a-Si interface passivation layer, J0s is significantly lower at 5.39 fA/cm2. The J0s and the ρc increase after post-deposition annealing. The evolution of these functional properties can be attributed to the material properties.
Description
Keywords
Citation
Collections
Source
Journal of Applied Physics
Type
Journal article
Book Title
Entity type
Access Statement
Open Access
License Rights
Restricted until
Downloads
File
Description