Tritium retention in W plasma-facing materials: Impact of the material structure and helium irradiation
Date
2019-05
Authors
Bernard, Elodie
Sakamoto, R
Hodille, Etienne
Kreter, Arkadi
Autissier, Emmanuel
Barthe, Marie-France
Desgardin, Pierre
Schwarz-Selinger, Thomas
Burwitz, Vassily Vadimovitch
Feuillastre, Sophie
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier Science
Abstract
Plasma-facing materials for next generation fusion devices, like ITER and DEMO, will be submitted to intense fluxes of light elements, notably He and H isotopes (HI). Our study focuses on tritium (T) retention on a wide range of W samples: first, different types of W materials were investigated to distinguish the impact of the pristine original structure on the retention, from W-coated samples to ITER-grade pure W samples submitted to various annealing and manufacturing procedures, along with monocrystalline W for reference. Then, He and He-D irradiated W samples were studied to investigate the impact on He-damages such as nano-bubbles (exposures in LHD or PSI-2) on T retention.
We exposed all the samples to tritium gas-loading using a gentle technique preventing any introduction of new damage in the material. Tritium desorption is measured by Liquid Scintillation counting (LSC) at ambient and high temperatures (800 °C). The remaining T inventory is then measured by sample full dissolution and LSC. Results on T inventory on He exposed samples highlighted that in all cases, tritium desorption as a gas (HT) increases significantly due to the formation of He damages. Up to 1.8 times more T can be trapped in the material through a competition of various mechanisms, but the major part of the inventory desorbs at room temperature, and so will most likely not take part to the long-term trapped inventory for safety and operational perspectives. Unfortunately, investigation of “as received” industrial W (used for the making of plasma-facing materials) highlighted a strong impact of the pre existing defects on T retention: up to 2.5 times more T is trapped in “as received W” compared to annealed and polish W, and desorbs only at 800 °C, meaning ideal W material studies may underestimate T inventory for tokamak relevant conditions.
Description
Keywords
Tungsten, Helium, Tritium inventory, Plasma-wall interactions
Citation
Collections
Source
Nuclear Materials and Energy
Type
Journal article
Book Title
Entity type
Access Statement
Open Access
License Rights
Creative Commons License (Attribution 4.0 International)
Restricted until
Downloads
File
Description