Ge11.5As24Se64.5 chalcognide glass nanowires with a nonlinear parameter of 136,000W-1km-1 at 1550nm

Gai, Xin; Madden, Steve; Bulla, Douglas; Luther-Davies, Barry; Choi, Duk-Yong


We have fabricated nanowires from Ge11.5As24Se64.5 glass. The loss of nanowire was measured to be 2.6dB/cm for fundamental TM mode. The nonlinear coefficient (γ) was determined to be ≈136±7W-1m-1 at 1550nm. Supercontinuum (SC) was produced in an 18mm

CollectionsANU Research Publications
Date published: 2010
Type: Conference paper
Source: 2010 conference on Optoelectronic and Microelectronic Materials and Devices Proceedings
DOI: 10.1109/COMMAD.2010.5699755


File Description SizeFormat Image
01_Gai_Ge11.5As24Se64.5_chalcognide_2010.pdf400.96 kBAdobe PDF    Request a copy
02_Gai_Ge11.5As24Se64.5_chalcognide_2010.pdf180.83 kBAdobe PDF    Request a copy
03_Gai_Ge11.5As24Se64.5_chalcognide_2010.pdf877.82 kBAdobe PDF    Request a copy

Items in Open Research are protected by copyright, with all rights reserved, unless otherwise indicated.

Updated:  17 November 2022/ Responsible Officer:  University Librarian/ Page Contact:  Library Systems & Web Coordinator