Rheology and nano-crystallization of a Zr 41.25 Ti 13.75 Ni 10 Cu 12.5 Be 22.5 bulk metallic glass
Creep of Zr-based bulk metallic glass (BMG) was carried out under hydrostatic pressure of 270 MPa superimposed on uniaxial compressive loads of 30-300 MPa. The temperature of testing was maintained at 633 K, which is close to the glass transition temperature of the BMG. The samples had heat treatment at 676 K for different lengths of time applied prior to testing, which resulted in microstructural changes. Apparent viscosity during flow was derived from the creep measurements. The effect of...[Show more]