Understanding the formation of (Al,Si)3Sc and V-phase (AlSc2Si2) in Al-Si-Sc alloys via ex situ heat treatments and in situ transmission electron microscopy studies
Dumbre, J.; Kairy, Shravan K; Anber, Elaf; Langan, Timothy; Taheri, Mitra L.; Dorin, T; Birbilis, Nick
Scandium (Sc) containing Al-Si model alloys were heat-treated at various temperatures to determine the interaction between Si and Sc. The (Al,Si)3Sc phase was formed at ~350 °C and V-phase (AlSc2Si2) was observed to form at above ~450 °C, as determined from x-ray diffraction and selected area electron diffraction. Hardening of the alloys was observed due to the formation of coherent, nanoscale (Al,Si)3Sc precipitates; whereas significant softening was observed upon the formation of coarse...[Show more]
|Collections||ANU Research Publications|
|Source:||Journal of Alloys and Compounds|
|1-s2.0-S092583882034874X-main.pdf||12.09 MB||Adobe PDF||Request a copy|
Items in Open Research are protected by copyright, with all rights reserved, unless otherwise indicated.
Updated: 17 November 2022/ Responsible Officer: University Librarian/ Page Contact: Library Systems & Web Coordinator